Radial Multilayer Ceramic Capacitor

  A leaded ceramic multilayer capacitor is a fixed capacitor with the ceramic material acting as the dielectric. It consists of several layers of conductive plates each separated by a layer of ceramic dielectric. Layers of ceramic and metal are alternated to make a multilayer chip. This chip equipped with lead wires and epoxy coated makes a Leaded MLCC.

 25 – 500 VDC
−55°C to +125°C operating temperature range
Capacitance offerings ranging from 10 pF up to 0.1μFThe capacitors consist of a general purpose MLCC.
The lead wires are 0.5 mm and are made of 100 % tinned copper clad steel wire. The capacitors may be supplied with straight or kinkedleads having a lead spacing of 2.5 mm and 5.0 mm. Coating is made of yellow colored flame retardant epoxy resin

6.3 – 500 VDC
−55°C to +125°C operating temperature range
Capacitance offerings ranging from 100 pF up to 22μFThe capacitors consist of a general purpose MLCC.
The lead wires are 0.5 mm and are made of 100 % tinned copper clad steel wire. The capacitors may be supplied with straight or kinkedleads having a lead spacing of 2.5 mm and 5.0 mm. Coating is made of yellow colored flame retardant epoxy resin

6.3 – 500 VDC
−55°C to +125°C operating temperature range
Capacitance offerings ranging from 220 pF up to220μFThe capacitors consist of a general purpose MLCC.
The lead wires are 0.5 mm and are made of 100 % tinned copper clad steel wire. The capacitors may be supplied with straight or kinkedleads having a lead spacing of 2.5 mm and 5.0 mm. Coating is made of yellow colored flame retardant epoxy resin

High operating temperature up to 200 °C 
25 – 200 VDC
Capacitance offerings ranging from 10pF up to 12nFThe capacitors consist of a general purpose MLCC.
The lead wires are 0.5 mm and are made of 100 % tinned copper clad steel wire. The capacitors may be supplied with straight or kinkedleads having a lead spacing of 2.5 mm and 5.0 mm. Coating is made of yellow colored flame retardant epoxy resin

500 – 3000 VDC
+10°C to +125°C operating temperature range
Capacitance offerings ranging from 12 pF to 0.1 μF
The capacitors consist of a general purpose MLCC.
The lead wires are 0.5 mm and are made of 100 % tinned copper clad steel wire. The capacitors may be supplied with straight or kinkedleads having a lead spacing of 2.5 mm and 5.0 mm. Coating is made of yellow colored flame retardant epoxy resin

25 – 200 VDC
−55°C to +150°C operating temperature range
 Capacitance offerings ranging from 1 pF to 0.22 μF
The lead wires are 0.5 mm and are made of 100 % tinned copper clad steel wire. The capacitors may be supplied with straight or kinkedleads having a lead spacing of 2.5 mm and 5.0 mm. Coating is made of yellow colored flame retardant epoxy resin